A set of chitosan samples irradiated by electrons with various doses were studied using the EPR method. Two kinds of paramagnetic defects PC1 and PC2 initiated by this irradiation due to the breakage of bonds in positions C5 and C1 of the chitosan structure are revealed in the "amorphous" and "crystalline" samples of chitosan. The structure of defects, their spectroscopic parameters, and kinetics of accumulation/decay have been established for the first time. It is found that EPR spectrum of the "crystalline" samples consists of 10 almost equidistant lines of the super-hyperfine (SHF) structure with the splitting between them A = 7,4 G for PC1 center, and a single wide line with the markedly different g-value, attributed to the PC2 one. Both these lines are also present in powder "amorphous" samples, but the SHF structure of the PC1 centers in them is not registered because of broadening the individual SHF components. Kinetics of defect accumulation with increasing dose D of the irradiation, and their gradual disappearance during prolonged storage of samples in air was discovered and studied. Kinetic equations were solved, and the D-dependence and decay times were found from the comparison of theoretical results with the experimental ones. It has been shown that the concentration of shallow and deep traps for electrons affect the rate of the decay process. The recovery process is much slower in the samples having a more perfect crystalline structure.

  Повний текст PDF - 618.579 Kb    Зміст випуску     Цитування публікації

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"