The heat capacity at constant pressure of fullerite C60 has been investigated using an adiabatic calorimeter in a temperature range from 1,2 to 120 K. Our results and literature data have been analyzed in a temperature interval from 0,2 to 300 K. The contributions of the intramolecular and lattice vibrations into the heat capacity of C60 have been separated. The contribution of the intramolecular vibration becomes significant above 50 K. Below 2,3 K the experimental temperature dependence of the heat capacity of C60 is described by the linear and cubic terms. The limiting Debye temperature at T -> 0 K has been estimated (THETA0 = 84,4 K). In the interval from 1,2 to 30 K the experimental curve of the heat capacity of C60 describes the contributions of rotational tunnel levels, translational vibrations (in the Debye model with THETA0 = 84,4 K), and librations (in the Einstein model with THETAE,lib = 32,5 K). It is shown that the experimental temperature dependences of heat capacity and thermal expansion are proportional in the region from 5 to 60 K. The contribution of the cooperative processes of orientational disordering becomes appreciable above 180 K. In the high-temperature phase the lattice heat capacity at constant volume is close to 4,5 R, which corresponds to the high-temperature limit of translational vibrations (3 R) and the near-free rotational motion of C60 molecules (1,5 R).

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Барабашко Максим Сергійович (фізико-математичні науки)
• Долбін Олександр Вітольдович (технічні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"