It is first determined by the semiempirical quantum chemical model MNDO for a carbon material (CM) structure based on polyacrylonitrile (PAN) heat-treated that the increase of a content N from 14 to 18 atoms in CM monolayers C₄₆N₁₄H₁₀, C₄₄N₁₆H₁₂, and C₄₂N₁₈H₁₄ and a content H from 12 to 22 atoms in CM monolayers C₄₄N₁₆H₁₂ and C₄₄N₁₆H₂₂ leads to the decrease of the binding energy (E_B) from 7,40; 7,12 to 6,88 and 6,25 eV, respectively; and to the increase of the differences between the maximum and minimum bond lengths (DELTA l), between the maximum and minimum valence angles (DELTA THETA), and between the maximum and minimum local charges (DELTA q) from 0,176 angstram; 12,0^o, and 0,487 to 0,238 angstram; 20,8^o, and 0,613, respectively, and promotes the CM structure curvature. Quantum chemical simulation results are confirmed by the element analysis of CM samples and a nanocomposite FeNi₃/C. As the IR heating temperature is increased from 30 to 500^o C, concenrations N (С_N) and H (C_H) in the CM and nanocomposite FeNi₃/C are decreased from 27 to 18 and 10 wt % and from 6 to 1 and 0,5 wt %, respectively.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Козлов Валерій Володимирович (військові науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"