X-ray diffraction and magnetic using dc and ac methods measurements of the polycrystalline and nanosize REMnO3 (RE = Pr, Nd) powdered samples have been performed. The nanosize manganites were synthesized with a sol-gel method at different (800, 850 and <$E900~symbol Р roman C>) temperatures. The average size of synthesized nanoparticles (from 56 to 89 nm) and polycrystalline powders (above 200 nm) was estimated using the x-ray diffraction data. All the compounds studied crystallize in the orthorhombic crystal structure (space group Pnma) at room temperature with smaller values of the lattice parameters in the nanosamples. The temperature-dependent ac magnetic susceptibilities show a sharp high-temperature peak connected with Mn magnetic moments ordering. The low-temperature maximum of magnetic susceptibility is proposed to be due to the polarization of the rareearth sublattice by an effective exchange field of the Mn ordered sublattice. The antiferromagnetic ordering of Mn sublattice and paramagnetic Curie temperatures as well as the magnetic moment values for the nanosize samples were found to be smaller than those for polycrystalline sample.

Індекс рубрикатора НБУВ: В371.236 + В377.3

Рубрики:

Магнітні властивості твердих тіл. Магнетики

Шифр НБУВ: Ж14063 Пошук видання у каталогах НБУВ 
Повний текст  Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Зубов Едуард Євгенович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"