Cadmium telluride (CdTe) polycrystalline films grown on glass ceramic substrates by a modified close-spaced vapor transport technique have been investigated. The as-grown films have columnar structure with the average grain sizes about 10 <$E mu roman m>. The in-plain direct current conductivity as a function of temperature and electric field has been investigated. The percolation conductivity is shown to be dominant at low temperatures (T << 250 K). At room temperature, the dominant transport mechanism is an activated process such as thermionic emission. The carrier transport across barriers is influenced by traps in the surface barrier regions. The non-annealed films exhibited stable electrical parameters and high photosensitivity during five-year storage under laboratory conditions.

Індекс рубрикатора НБУВ: В379.226

Рубрики:

Тонкі шари напівпровідників

Шифр НБУВ: Ж16425 Пошук видання у каталогах НБУВ 
Повний текст  Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Сукач Андрій Васильович (фізико-математичні науки)
• Тетьоркін Володимир Володимирович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"