The objective of this paper is the analysis of damage level of steam pipeline steel 14MoV63, in the conditions of the crack growth initiation by ductile fracture mechanism. The state of the material after about 100 000 service hours in the power plant has been estimated using a combined experimental and numerical procedure, based on the local approach to fracture. The level of damage has been determined by the analysis of the material taken from the pipeline (aged) and new (virgin) material of the same grade for comparison. The critical values of J-integral have been determined on single-edge notched bend (SENB) specimens experimentally and using a simplified procedure of local approach without the knowledge of the microstructural parameters. Two micromechanical models have been used: Rice - Tracey, modified by Beremin (uncoupled) and Complete Gurson Model (CGM) (coupled).

Індекс рубрикатора НБУВ: К222.234.106 + З370.5-03

Рубрики:

Властивості сталі для енергетичного обладнання

Трубопроводи теплових електричних станцій

Шифр НБУВ: Ж29109 Пошук видання у каталогах НБУВ 

---

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"