The materials with GMR are promising for magnetic sensor and other applications. We studied influence of dielectric matrix on GMR effect in granular films. Granular films of composition (FeCo)x(HfO2)1-x were prepared by electron-beam co-evaporation of FeCo and dielectric HfO2 in vacuum 10<^>-6 Pa. Electrical resistance was measured with standard four-lead technique. The percolation threshold for (FeCo)x(HfO2)1-x films was determined from electrical resistance measurements. The electrical resistance fast will increase at a content HfO2 of the order 20 vol. %. The GMR effect was observed in region of percolation transition (~ 20 vol. % HfO2). This result is similar to result for granular films with nonmagnetic metal matrix. In this region of concentration magnetic particles are in a nonmagnetic metal or dielectric matrix. The mechanisms of conductivity are different in these cases but GMA does not depend on a nature of nonmagnetic matrix.

Індекс рубрикатора НБУВ: К222.026 + К235.160.26

Шифр НБУВ: Ж14161 Пошук видання у каталогах НБУВ 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Кравець Анатолій Федорович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"